Chemical Consequences of Alkali Inhomogeneity in Cu 2 ZnSnS 4 Thin‐Film Solar Cells

This study offers new insight into the role of Na in Cu 2 ZnSnS 4 (CZTS) thin film solar cells by studying samples with a spatially varying alkali distribution. This is achieved by omitting a diffusion barrier between the soda‐lime glass substrate and the Mo back contact, where compositional variations of the glass inherently result in non‐uniform alkali distributions in the CZTS. By correlating light beam induced current (LBIC) maps with secondary ion mass spectrometry composition maps, it is shown that samples containing regions of higher Na concentration (“hot spots”) have corresponding LBIC hot spots on comparable length scales. Samples containing an alkali diffusion barrier have lower LBIC dispersion; thus, LBIC can be used to evaluate non‐uniformity in CZTS devices, where a common cause is Na inhomogeneity. Moreover, it is shown that the Na hot spots are strongly correlated with ot…