Large-Scale Synthesis of Carbon-Shell-Coated FeP Nanoparticles for Robust Hydrogen Evolution Reaction Electrocatalyst

A highly active and stable non-Pt electrocatalyst for hydrogen production has been pursued for a long time as an inexpensive alternative to Pt-based catalysts. Herein, we report a simple and effective approach to prepare high-performance iron phosphide (FeP) nanoparticle electrocatalysts using iron oxide nanoparticles as a precursor. A single-step heating procedure of polydopamine-coated iron oxide nanoparticles leads to both carbonization of polydopamine coating to the carbon shell and phosphidation of iron oxide to FeP, simultaneously. Carbon-shell-coated FeP nanoparticles show a low overpotential of 71 mV at 10 mA cm –2, which is comparable to that of a commercial Pt catalyst, and remarkable long-term durability under acidic conditions for up to 10 000 cycles with negligible activity loss. The effect of carbon shell protection was investigated both theoretically and experimentally. A …